Stainless Steel 904L Instrumentation Ball Valve

  • Home /
  • Stainless Steel 904L Ball Valve
Stainless Steel 904L Ball Valve

 

STANDARD  API 600/BS1414, API 598/BS EN 12266-1, ASME B 16.10, ASME B 16.5, ASME B 16.25, ASME B 16.34
VALVE SIZE 1/8" TO 2" / 6 MM TO 50 MM
THREAD NPT, BSPP, BSPT, JIC, METRIC, UNF
CONNECTION THREADED, TUBE END, BUTT WELD, SOCKET WELD, WELD NIPPLE, FLANGED, SAE
FUNCTION 2 WAY, 3 WAY, 4 WAY, 5 WAY, 
PRESSURE RATING 1500 PSI, 3000 PSI, 6000 PSI, 10000 PSI, 15000 PSI, 20000 PSI
SEAL RING MATERIAL PTFE, PVDF, DELRIN, PEEK, GRAPHITE
STANDARD ISO , DIN , ANSI , API , ASME , AWWA , MSS , 
MEDIA  HYDRAULIC OIL, AIR, WATER, GAS, STEAM, HOT WATER , COLD WATER , SEA WATER , CHEMICAL
MEDIA TEMPERATURE (-120* C TO 500*C )RANGE AS PER PRESSURE
BODY TYPE BAR STOCK
BRAND NAME TU-LOK
PACKING DETAILS BOX PACKING, WOODEN PALLET
EQUIVALENT BRANDS SWAGELOK, PARKER, DK-LOK, HAMLET, OLIVER VALVES, HOKE
APPLICATION MATERIAL HANDLING EQUIPMENT, EARTH MOVING MACHINERIES , POWER GENERATING PLANT , STEEL MANUFACTURING PLANT , MINING INDUSTRIES , CHEMICAL PROCESSING MACHINES , PIPING LINE ,  PAINT INDUSTRIES , TRUCKS AND TRAILERS , AUTOMATION , AGRICULTURE MACHINES , AEROSPACE & DEFENCE EQUIPMENTS, 

 

904l High Pressure Ball Valve

904l High Pressure Ball Valve

904l Instruemntation Ball Valve

904l Instruemntation Ball Valve

904l Panel Mounted Ball Valve

904l Panel Mounted Ball Valve


Tensile Strength (MPa) min
Yield Strength 0.2% Proof (MPa) min
Elongation (% in 50mm) min
Hardness
Rockwell B (HR B)
Hardness
Brinell (HB)
490
220
36
70-90 typical
150

 

C Mn Si P S Cr Mo Ni Cu
0.02 Max 2.0 Max 1.0 Max 0.045 Max 0.035 Max 19.0 Min
23.0 Max
4.0 Min
5.0 Max
23.0 Min
28.0 Max
1.0 Min
2.0 Max

 

Grade
904L
Density
(kg/m3)
7900
Elastic Modulus
(GPa)
190
Mean Co-eff of Thermal Expansion (µm/m/°C)
0-100°C
15
0-315°C
0-538°C
Thermal Conductivity
(W/m.K)
At 20°C
11.5
At 500°C
Specific Heat 0-100°C
(J/kg.K)
500
Elec Resistivity
(nΩ.m)
952

 

  • Non-magnetic
  • Stronger corrosion properties than Type 316L an 317L
  • Good resistance to sulphuric, phosphoric and acetic acids
  • High resistance to crevice and stress corrosion cracking
  • Excellent formability and weldability