BRAND | TU-LOK |
DESIGN STANDARD | DIN 2353/ ISO 8434-1 |
MATERIAL | SS 316TI ( 1.4571) |
SERIES | LL- LOW PRESSURE , L- MEDIUM PRESSURE, S- HIGH PRESSURE |
WORKING PRESSURE | (LOW) LL SERIES - 100 BAR |
(MEDIUM)L SERIES - 100 BAR TO 500 BAR | |
(HEAVY)S SERIES - 200 BAR TO 800 BAR | |
SIZE RANGE | LL SERIES - 4LL TO 12LL |
L SERIES - 6L TO 42L | |
S SERIES - 6S TO 38S | |
CONNECTIONS | TUBE TO TUBE , TUBE TO MALE THREAD , TUBE TO FEMALE THREAD , TUBE TO BUTT WELD , TUBE TO SOCKET WELD , TUBE TO JIC 37* , TUBE TO 24* CONE, TUBE TO SWIVEL END , TUBE TO ADJUSTBALE STANDPIPE |
WELD NIPPLE TO MALE THREAD , WELD NIPPLE TO FEMALE THREAD , WELD NIPPLE TO BUTT WELD , WELD NIPPLE TO SOCKET WELD , WELD NIPPLE TO 24* CONE , WELD NIPPLE TO 37* JIC , WELD NIPPLE TO SWIVEL | |
BODY TYPE | FORGED, BAR STOCK |
ACCESSORIES | O-RING, DOWTY SEAL , COPPER WASHER , ED SEAL, CUTTING RING , NUT |
O-RING & SEALS | NBR ( -35*C TO 100* C ) VITON (-25*C TO 200* C) , PTFE - (-60*C TO 240*) |
SURFACE | STAINLESS STEEL 316 TI - EXPORT BRIGHT FINISH, SHORT BLASTED FINISH, ELECTROPLATED FINISH |
TEMPERATURE | STAINLESS STEEL - (-60*C TO 400*C) |
EQUIVALENT BRANDS | PARKER, HY-LOK , DK-LOK , STAUFF, HYDAC , VOSS |
MATERIAL DESIGNATOR | STAINLESS STEEL - ASTM A 276 , ASTM 182 |
Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
8.0 g/cm3 | 1399 °C (2550 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35 % |
STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
SS 316TI | 1.4571 | S31635 | SUS 316Ti | 320S31 | 08Ch17N13M2T | Z6CNDT17‐123 | X6CrNiMoTi17-12-2 |
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N |
SS 316TI | 0.08 max | 2 max | 0.75 max | 0.045 max | 0.030 max | 16.00 – 18.00 | 2.00 – 3.00 | 10.00 – 14.00 | 68.395 min |