Sanicro 28 Instrumentation Ball Valve

  • Home /
  • Sanicro 28 Ball Valve
Sanicro 28 Ball Valve
VALVE SIZE 1/8" TO 2" / 6 MM TO 50 MM
THREAD NPT, BSPP, BSPT, JIC, METRIC, UNF
CONNECTION THREADED, TUBE END, BUTT WELD, SOCKET WELD, WELD NIPPLE, FLANGED, SAE
FUNCTION 2 WAY, 3 WAY, 4 WAY, 5 WAY, 
PRESSURE RATING 1500 PSI, 3000 PSI, 6000 PSI, 10000 PSI, 15000 PSI, 20000 PSI
SEAL RING MATERIAL PTFE, PVDF, DELRIN, PEEK, GRAPHITE
STANDARD ISO , DIN , ANSI , API , ASME , AWWA , MSS , 
MEDIA  HYDRAULIC OIL, AIR, WATER, GAS, STEAM, HOT WATER , COLD WATER , SEA WATER , CHEMICAL
MEDIA TEMPERATURE (-120* C TO 500*C )RANGE AS PER PRESSURE
BODY TYPE BAR STOCK
BRAND NAME TU-LOK
PACKING DETAILS BOX PACKING, WOODEN PALLET
EQUIVALENT BRANDS SWAGELOK, PARKER, DK-LOK, HAMLET, OLIVER VALVES, HOKE
APPLICATION MATERIAL HANDLING EQUIPMENT, EARTH MOVING MACHINERIES , POWER GENERATING PLANT , STEEL MANUFACTURING PLANT , MINING INDUSTRIES , CHEMICAL PROCESSING MACHINES , PIPING LINE ,  PAINT INDUSTRIES , TRUCKS AND TRAILERS , AUTOMATION , AGRICULTURE MACHINES , AEROSPACE & DEFENCE EQUIPMENTS, 

 

STANDARD WERKSTOFF NR. UNS EN AFNOR
Sanicro 28 1.4563 N08028 X1NiCrMo31-27-4 Z1NCDU31-27-03

 

Tensile Strength Elongation Yield Strength
(0.2%Offset)
Hardness
500-750 35% 220 230

 

C Si Mn P S Cr Ni Mo Cu N
≤0.020 ≤0.7 ≤2.0 ≤0.020 ≤0.010 27 31 3.5 1.0 ≤0.1

 

Principal Design Features Sanicro 28 is a precipitation, age hardenable stainless steel. It's principal features are high transverse toughness, good resistance to general and stress corrosion cracking, and high strength that is developed by a single low temperature heat treatment.
Stainless Steel Sanicro 28 Applications This alloy has been used in aircraft components such as landing gear and structural sections, valves, shafts, and components in the petrochemical and nuclear industries.
Stainless Steel Sanicro 28 Machinability This is a tough machining stainless steel. Although it can be machined in all conditions, best results can be obtained in condition H1150M. Compared to type 304 stainless, speeds should be roughly 25 % lower for optimum tool life and finish.
Stainless Steel Sanicro 28 Forming This alloy can be formed using conventional techniques with the degree of formability being limited only by its high initial yield strength.
Stainless Steel Sanicro 28 Welding Best welded in the solution annealed condition, using Sanicro 28 filler material. Both resistance and inert gas shielded methods are acceptable.
Stainless Steel Sanicro 28 Heat Treatment CONDITION A--Soak at 1700 F (927 C) and cool below 60 F (16 C) for 1 hour. CONDITION RH 950- Treat Condition A material at -100 F(-73C) for 2 hours, air warm to room temperature (within 24 hours of solution treatment). Then heat cold treated material to 950 F(510 C) for 4 hours and air cool. CONDITION H950, H1000, H1050, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Stainless Steel Sanicro 28 Forging Soak at 2150 F(1177 C) for 1 hour prior to forging. Do not work below 1750 F(954 C). All forgings should be solution treated prior to final hardening. Air cool to room temperature after forging.
Stainless Steel Sanicro 28 Hot Working 13-8 can be satisfactorily hot worked. Hot worked material must be solution annealed prior to hardening for reliable results.
Stainless Steel Sanicro 28 Cold Working Despite its high initial yield strength, this alloy can be satisfactorily cold worked.